שימוש ביתד עם חומרים מרוכבים לשחזור לאחר טש

שימוש ביתד עם חומרים מרוכבים לשחזור לאחר טש. אינו מוסיף לחוזק של השחזור.

נבחנו צורות יתד שונות ממתכת ומסיבי זכוכית  .הכישלון הוא תמיד בחיבור בין השן לשחזור .

כאמור השימוש ביתד לא הוסיף לחוזק אך בהחלט גרם להחלשות השורש ,עובדה המעמידה

בסימן שאלה את נחיצות השימוש ביתדות בשימוש עם חומרים מרוכבים .

מתוך הג’ורנאל:















International Endodontic Journal
Volume 38 Issue 4 Page 230  – April 2005
doi:10.1111/j.1365-2591.2005.00941.x

אבסטרקט המאמר:


Ex vivo fracture resistance of direct resin composite complete crowns with and without posts on maxillary premolars


W. A. Fokkinga1, A.-M. Le Bell2, C. M. Kreulen1, L. V. J. Lassila2, P. K. Vallittu2 & N. H. J. Creugers1






Aim To investigate ex vivo the fracture resistance and failure mode of direct resin composite complete crowns with and without various root canal posts made on maxillary premolars.premolars

Methodology The clinical crowns of 40 human extracted single-rooted maxillary premolars were sectioned at the cemento-enamel junction. The canals were prepared with Gates Glidden drills up to size 4. Thirty samples were provided with standardized post spaces in the palatal canal and all roots were embedded in acrylic. Minimal standardized preparations in the canal entrances were made. Groups of 10 samples were treated with (i) prefabricated metal posts, (ii) prefabricated glass fibre posts, (iii) custom-made glass fibre posts, and (iv) no posts (control). Posts were cemented with resin cement and resin composite complete crowns were made. All specimens were thermocycled (6000x, 5-55 °C). Static load until fracture was applied using a universal loading device (crosshead speed 5 mm min-1) at a loading angle of 30°. Failure modes were categorized as favourable and unfavourable failures.

Results No significant difference was observed between the mean failure loads (group 1: 1386 N, group 2: 1276 N, group 3: 1281 N, and group 4: 1717 N, P > 0.05), nor between frequencies of failure modes (P > 0.05). All failures were fractures of the resin composite crown in combination with tooth material (cohesive failures).

Conclusions Within the limits of this laboratory investigation it is concluded that severely damaged and root filled maxillary premolars, restored with direct resin composite complete crowns without posts have similar fracture resistances and failure modes compared to those with various posts, which suggest that posts are not necessarily required.


תגובות רוצה להצטרף לדיון?

אין תגובות עדיין. היה הראשון להגיב!

מאמרים

לכל המאמרים

כניסת צוות רפואי

הכניסה לאתר מותרת אך ורק לצוות הרפואי

לקבלת קוד אימות לנייד ולמייל, יש למלא את כתובת המייל ואת מספר הטלפון שלך

עדיין לא נרשמת? באפשרותך לבצע רישום כאן